Stainless Steel Grade 410S

Grade 201 stainless steel has potential formability, corrosion resistance, and fabricability. It is quite similar to  301 stainless steel. The following Resources give some more details about grade 201 stainless steel.

Grade 201 stainless steel is used for various purposes, like many kinds of severely formed parts, roofing for railway trailers and cars to siding can be used for welding

326b-tubing-e1586378695741.jpg
Stainless-Steel-Sheet.jpg
Stainless-Steel-Materials-Ss201-SS304-SS316-SS316L-Ss321-Ss430.jpg
wedsit photos.jpg
1-500x500.jpg

Equivalent Grades Of Stainless Steel 410S

  • DIN 1.4034

  • ASME SA240

  • ASTM A176

  • SAE 51410S

Some, of the equivalent grades of Stainless 410S Are:-

  • ASTM A240

  • ASTM A473

  • DIN 1.0400

  • DIN 1.4001

Chemical Composition Of Stainless Steel 410S

This is the chemical Composition of Stainless Steel 410S.

Element                                                                                                                                 Content (%)

Iron,Fe                                                                                                                                             85

Chromium, Cr                                                                                                                            12.5

Manganese, Mn                                                                                                                           1.0

Silicon, Si                                                                                                                                       1.0

Carbon, C                                                                                                                                    0.080

Phosphorous, P                                                                                                                        0.040

Sulfur, S                                                                                                                                       0.030

Physical Properties Of Stainless Steel 410S

This is the ​​Physical Properties of Stainless Steel 410S.

Properties                                                        Metric                                            Imperial

Density                                                           7.80 g/cm                                        0.282 lb/in³

Melting point                                                 1532°C                                                  2790°F

Mechanical Properties Of Stainless Steel 410S

                                              Properties                                                              Metric          Imperial

Tensile strength                                                                                               1525 MPa     221200 psi

Yield strength (@strain 0.200%)                                                              1225 MPa     177700 psi

Elastic modulus                                                                                           190-210 GPa   27557-30458k

Poisson's ratio                                                                                                           0.27-0.30       0.27-0.30

Elongation at break (in 50 mm)                                                                   14.50%          14.50%

Hardness, Knoop (converted from Rockwell C hardness)                 464                 464

Hardness, Rockwell C                                                                                           45                   45

Hardness, Vickers (converted from Rockwell C hardness)               446                 446

Thermal Properties Of Stainless Steel 410S

Properties                                                          Metric                                           Imperial

Thermal expansion co-efficient            9.90 µm/m°C                          5.50 µin/in°F

Thermal (@ 100°C/212°F)                          24.9 W/mK                       173 BTU in/hr.ft².°F