Stainless Steel Grade 439

Stainless steel grade 439 is capable of being made into complex shapes such as tubular manifolds and exhaust system components, where temperatures tend to go beyond the oxidation limit of grade 409 steel. It is also preferred where wet corrosion resistance especially to chlorides is needed.

Stainless steel grade 439 has good weldability, brightness, and pitting corrosion resistance. It polishes well, and is good for deep drawing.

326b-tubing-e1586378695741.jpg
Stainless-Steel-Sheet.jpg
Stainless-Steel-Materials-Ss201-SS304-SS316-SS316L-Ss321-Ss430.jpg
wedsit photos.jpg
1-500x500.jpg

Equivalent Grades Of Stainless Steel 439

Some, of the equivalent grades of Stainless 439 Are:-

  • DIN 1.4510.

Chemical Composition Of Stainless Steel 439

This is the chemical Composition of Stainless Steel 439

Element                                                                                                                                 Content (%)

Iron,Fe                                                                                                                                        81.3535

Chromium, Cr                                                                                                                            17.35

Manganese, Mn                                                                                                                          0.25

Nickel, Ni                                                                                                                                       0.20

Silicon, Si                                                                                                                                      0.35

Nitrogen, N                                                                                                                                 0.0100

Carbon, C                                                                                                                                      0.01

Phosphorous, P                                                                                                                          0.02     

Sulfur, S                                                                                                                                      0.0015

Niobium, Nb (columbium, Cb)                                                                                           0.01

Molybdenum, Mo                                                                                                                      0.10
Titanium, Ti                                                                                                                                 0.335

Mechanical Properties Of Stainless Steel 439

                                              Properties                                                              Metric          Imperial

Tensile strength (transverse at room temperature)                        685 MPa       99400 psi

Tensile strength (longitudinal at room temperature)                    696 MPa      101000 psi

Yield strength (transverse at room temperature)                             292 MPa       42400 psi

Yield strength (longitudinal at room temperature)                         301 MPa      43700 psi

Compressive yield strength                                                                         365 MPa      52900 psi

Elastic modulus                                                                                                 197GPa        28573 ksi

Poisson's ratio                                                                                                   0.27-0.30       0.27-0.30

Elongation at break (longitudinal at room temperature)                   56%              56%

Elongation at break (transverse at room temperature)                     62.50%        62.50%

Hardness, Rockwell B (transverse at room temperature)                     85                  85

Hardness, Rockwell B (longitudinal at room temperature)                 85                  85

Thermal Properties Of Stainless Steel 439

Properties                                                          Metric                                           Imperial

Thermal expansion co-efficient            16.6 µm/m°C                          9.22 µin/in°F

Thermal (@ 100°C/212°F)                          16.3 W/mK                       113 BTU in/hr.ft².°F