Stainless Steel Grade Duplex 2101 LDX (UNS S32101)

Stainless steel grade Duplex 2101 LDX is a low-alloyed, general-purpose duplex. This steel possesses high tensile strength as well as high fatigue strength. Its high mechanical strength is the same as other duplex grades, and its good corrosion resistance is equal to most standard stainless steel grades. All these properties are utilized to design products with strength, low maintenance, durability, and long-term cost efficiency.

wedsit photos.jpg

Chemical Composition Of Stainless Steel 
Duplex 2101 LDX (UNS S32101)

This is the chemical Composition of Stainless Steel Duplex 2101 LDX (UNS S32101)

Element                                                                                                                                 Content (%)

Iron,Fe                                                                                                                                            71.45

Chromium, Cr                                                                                                                             21.50

Manganese, Mn                                                                                                                              5

Nickel, Ni                                                                                                                                         1.5

Molybdenum, Mo                                                                                                                        0.3

Nitrogen, N                                                                                                                                  0.220

Carbon, C                                                                                                                                      0.03

Mechanical Properties Of Stainless Steel 
Duplex 2101 LDX (UNS S32101)

                                              Properties                                                              Metric          Imperial

Tensile Strength (annealed)                                                                       696 MPa     101000 psi

Yield strength (@strain 0.200%)                                                               450 MPa     65300 psi

Modulus of elasticity                                                                                       200 GPa      29000 ksi

Shear modulus                                                                                                   77 GPa         11200 ksi

Poisson's ratio                                                                                                        0.30               0.30

Elongation at break (In 2", 50% cold worked)                                         38%                38%