Stainless Steel Grade 309S

Stainless steels are called as high-alloy steels. Due to the presence of large amounts of chromium in the range of 4 to 30%, they have high corrosion resistance than other steels. Stainless steels are classified into martensitic, ferritic and austenitic based on their crystalline structure. However, stainless steels present in the form of a combination of martensitic and austenitic steels are known as precipitation-hardened steels.

The following datasheet will provide more details about grade 305 stainless steel, which has high resistance to heat and corrosion.

326b-tubing-e1586378695741.jpg
Stainless-Steel-Sheet.jpg
Stainless-Steel-Materials-Ss201-SS304-SS316-SS316L-Ss321-Ss430.jpg
wedsit photos.jpg
1-500x500.jpg

Equivalent Grades Of Stainless Steel 309S

  • ASTM A314

  • ASTM A473

  • ASTM A479

  • ASTM A511

  • ASTM A554

  • ASTM A580

  • ASTM A813

  • ASTM A814

  • DIN 1.4833

Some, of the equivalent grades of Stainless 309S Are:-

  • AMS 5523

  • AMS 5574

  • AMS 5650

  • ASTM A167

  • ASTM A213

  • ASTM A240

  • ASTM A249

  • ASTM A276

  • ASTM A312

Chemical Composition Of Stainless Steel 309S

This is the chemical Composition of Stainless Steel 309S.

Element                                                                                                                                 Content (%)

Iron,Fe                                                                                                                                            60

Chromium, Cr                                                                                                                             23

Manganese, Mn                                                                                                                          02

Nickel, Ni                                                                                                                                       14

Silicon, Si                                                                                                                                      01

Nitrogen, N                                                                                                                                   00

Carbon, C                                                                                                                                   0.080

Phosphorous, P                                                                                                                       0.045

Sulfur, S                                                                                                                                      0.030

Physical Properties Of Stainless Steel 309S

This is the ​​Physical Properties of Stainless Steel 309S.

Properties                                                      Metric                                             Imperial

Density                                                             8 g/cm                                            0.289 lb/in³

Melting point                                                 1454°C                                                2650°F

Mechanical Properties Of Stainless Steel 309S

                                              Properties                                                              Metric          Imperial

Tensile strength, ultimate                                                                            620 MPa      89900 psi

Tensile strength, yield (0.2%)                                                                     310 MPa      45000 psi

Izod impact                                                                                                          120-165J   88.5-122ft-lb

Modulus of elasticity                                                                                       200 GPa      29000 ksi

Shear modulus                                                                                                    77 GPa        11200 ksi

Poissons ratio                                                                                                          0.3                    0.3

Elongation at break (in 50 mm)                                                                      45%                 45%

Hardness, Brinell (converted from Rockwell B hardness)                 147                   147

Hardness, Knoop (converted from Rockwell B hardness)                 164                   164

Hardness, Rockwell B                                                                                          85                      85

Hardness, Vickers (converted from Rockwell B hardness)               169                    169

Thermal Properties Of Stainless Steel 309S

Properties                                                          Metric                                           Imperial

Thermal expansion co-efficient            14.9 µm/m°C                          9.22 µin/in°F

Thermal (@ 100°C/212°F)                          15.6 W/mK                       108 BTU in/hr.ft².°F